SBA15 mesoporous molecular sieves are a kind of synthesis it is the rise in recent years, another important chemical technology, in catalysis, separation, bio-and nano-material, and a wide range of applications, and its high hydrothermal stability advantages of catalysis, adsorption and separation of inorganic materials and other disciplines to develop advanced new research field. It can be expected, with the deepening of research for SBA15, the results inevitably in the chemical industry has a new breakthrough.
Synthesis Mesoporous SBA-15 synthesis is typical: in 35-40 ℃ under the conditions of the triblock surfactant P123 (Aldrich, EO20PO70EO20, Ma = 5800) dissolved in deionized water, added to which are silicon acid ethyl ester (TEOS), hydrochloric acid (HCl), vigorous stirring continued for more than 24h, 24h crystallized into more than ethylene bottle, filtered, washed and dried, and finally calcined at 550 ℃ for more than 5h to remove the template agent or washing with solvent reflux to the template, and then filtered, washed and dried, the resulting white powder is the SBA-15. The raw materials used in the experiment the molar ratio of about 1TEOS: 0.017P123: 5.88HCl: 136H2O.
Synthesis Mechanism Mesoporous SBA-15 synthesis in line with the neutral template mechanism (S0I): neutral surfactant P123 (S0), and neutral inorganic silicon species (I0) through hydrogen bonding, there is strong electrostatic interaction, and further hydrolyzed with silanols and condensation lead to the accumulation of short-range hexagonal particles and the formation of the skeleton. SBA-15 synthesis under mild conditions, easy to remove the surfactant, and are unlikely to cause structural collapse; neutral surfactants and neutral inorganic precursor than the repulsive force between ionic surfactant and inorganic precursors with charge repulsion force is much smaller, can form a thick cell wall, thereby increasing the zeolite framework structure of the thermal and hydrothermal stability.
Affect FactorsAffect the mesoporous SBA-15 structure of many factors, mainly the following aspects: Templin M, franck A and other studies have shown that organic copolymer as a template by changing its own chemical structure, chain length, functional groups, to regulate product size, mechanical and thermal performance purposes. Zhao and other used a new method - the co-solvent method to control the appearance of mesoporous materials and shape of particles. As in N, N-dimethylformamide (DMF) solvent were obtained for the highly ordered, large aperture, "donut"-like mesoporous SBA-15. By controlling the total amount of solvent added, polarity, etc. can also change the size of SBA-15 morphology, such as the common solvent THF can be synthesized as "intestinal egg"-like SBA-15. By selecting the silicon source, adding additives to control the morphology of SBA-15. If you choose to use fat as the silicon is silica source has been the "wheat-like" SBA-15; choose is acid methyl ester as a silicon source to get the "cashew-like" SBA-15; added electrolytes, such as K2SO4, will be a round sheet SBA-15. Kohji Miyazawa and Shinji Inagaki synthesized by changing the temperature and the silicon source and template to control the ratio of SBA-15 pore volume and porosity, they pointed out that the temperature is higher than 100 ℃, can not be synthesized mesoporous SBA-15, increasing the silicon source compared with the template agent is an effective way to increase the pore volume. Y Bennadja, P Beaunier, who also observed that inorganic and organic precursors very close relationship between the precursor for synthesis of SBA-15 has a great impact. Ye Wang, Masato Noguchi synthetic aperture in the SBA-15 is adjustable between 3.6-12nm, they are joined trimethylbenzene as the expansion agent use increased after the aperture synthesis method of heat treatment.
Read more: Buy A SBA15
Synthesis Mesoporous SBA-15 synthesis is typical: in 35-40 ℃ under the conditions of the triblock surfactant P123 (Aldrich, EO20PO70EO20, Ma = 5800) dissolved in deionized water, added to which are silicon acid ethyl ester (TEOS), hydrochloric acid (HCl), vigorous stirring continued for more than 24h, 24h crystallized into more than ethylene bottle, filtered, washed and dried, and finally calcined at 550 ℃ for more than 5h to remove the template agent or washing with solvent reflux to the template, and then filtered, washed and dried, the resulting white powder is the SBA-15. The raw materials used in the experiment the molar ratio of about 1TEOS: 0.017P123: 5.88HCl: 136H2O.
Synthesis Mechanism Mesoporous SBA-15 synthesis in line with the neutral template mechanism (S0I): neutral surfactant P123 (S0), and neutral inorganic silicon species (I0) through hydrogen bonding, there is strong electrostatic interaction, and further hydrolyzed with silanols and condensation lead to the accumulation of short-range hexagonal particles and the formation of the skeleton. SBA-15 synthesis under mild conditions, easy to remove the surfactant, and are unlikely to cause structural collapse; neutral surfactants and neutral inorganic precursor than the repulsive force between ionic surfactant and inorganic precursors with charge repulsion force is much smaller, can form a thick cell wall, thereby increasing the zeolite framework structure of the thermal and hydrothermal stability.
Affect FactorsAffect the mesoporous SBA-15 structure of many factors, mainly the following aspects: Templin M, franck A and other studies have shown that organic copolymer as a template by changing its own chemical structure, chain length, functional groups, to regulate product size, mechanical and thermal performance purposes. Zhao and other used a new method - the co-solvent method to control the appearance of mesoporous materials and shape of particles. As in N, N-dimethylformamide (DMF) solvent were obtained for the highly ordered, large aperture, "donut"-like mesoporous SBA-15. By controlling the total amount of solvent added, polarity, etc. can also change the size of SBA-15 morphology, such as the common solvent THF can be synthesized as "intestinal egg"-like SBA-15. By selecting the silicon source, adding additives to control the morphology of SBA-15. If you choose to use fat as the silicon is silica source has been the "wheat-like" SBA-15; choose is acid methyl ester as a silicon source to get the "cashew-like" SBA-15; added electrolytes, such as K2SO4, will be a round sheet SBA-15. Kohji Miyazawa and Shinji Inagaki synthesized by changing the temperature and the silicon source and template to control the ratio of SBA-15 pore volume and porosity, they pointed out that the temperature is higher than 100 ℃, can not be synthesized mesoporous SBA-15, increasing the silicon source compared with the template agent is an effective way to increase the pore volume. Y Bennadja, P Beaunier, who also observed that inorganic and organic precursors very close relationship between the precursor for synthesis of SBA-15 has a great impact. Ye Wang, Masato Noguchi synthetic aperture in the SBA-15 is adjustable between 3.6-12nm, they are joined trimethylbenzene as the expansion agent use increased after the aperture synthesis method of heat treatment.
Read more: Buy A SBA15
No comments:
Post a Comment